Microporous alumina membranes electrochemically grown
2003
Abstract The electrochemical fabrication of alumina membranes by anodizing of aluminium in phosphoric acid and oxalic acid solutions, in the temperature interval from −1 to 16 °C, was investigated in order to study the influence of different parameters (initial treatment of aluminium surface, nature and composition of electrolyte, temperature) on the final characteristics of the membranes. Porous layers were grown using a linear potential scan at 0.2 V s −1 up to 160 V in H 3 PO 4 solution and 70 V in oxalic acid solution. The efficiency of porous layer formation was calculated by using Faraday's law and weight measurements. Pore size distribution and porosity of membranes prepared in 0.4 M…
Electrodeposition of CeO2 and Co-Doped CeO2 Nanotubes by Cyclic Anodization in Porous Alumina Membranes
2013
An anodic electrodeposition process is proposed to prepare CeO2 and Co-doped CeO2 nanotubes. Anodic alumina membrane is used as template and linear sweep voltammetry is employed to allow the formation of nanotubes without alumina dissolution. SEM micrographs showed large arrays of well defined and aligned NTs, which resulted to be crystalline soon after deposition according to XRD diffraction patterns and Raman Spectroscopy.
Comments on 'formation and characterization of nanotubes of La(OH) 3 obtained using porous alumina membranes'
2010
New experimental evidence concerning the formation of La(OH)3 nanowires on anodic alumina membranes by cathodic polarization in 0.05 M lanthanum nitrate solution is provided to further support the conclusions previously reached in our work (Bocchetta et al 2007 Electrochem. Commun. 9 683-8) and recently criticized by González-Rovira et al (Nanotechnology 2008 19 495305). Some unconvincing aspects of the paper of González-Rovira et al, according to which the same electrochemical process should lead to the formation of hydroxycarbonate nanotubes, are also discussed.
Cs0.86(NH41.14SO4Te(OH)6 in porous anodic alumina for micro fuel cell applications.
2011
Abstract Cs0.86(NH4)1.14SO4Te(OH)6 supported by anodic alumina membranes (AAMs) has been characterized for the first time in H2/O2 fuel cell. The fabricated membrane electrode assemblies are able to produce peak power densities in the range 15–30 mW cm−2 under mild conditions (room temperature, low humidity and low Pt loading) and show an increased durability with cycling with respect to previous results obtained with AAM-based fuel cell. The physico-chemical characterization of the electrolytes has been carried out through X-ray diffractometry, scanning electron microscopy and micro-raman analysis. An estimation of the composite membranes conductance under fuel cell operation has been carr…